CONSTRUCTION
Style NA1100
is a compressed non-asbestos
sheet gasket material produced from carbon fibers and graphite,
bonded with nitrile rubber (NBR). It is manufactured through the hot
calendar process under rigorous quality control standards that are
registered under ISO-9001 certification.
APPLICATION / SERVICE
Style NA1100
is a premium grade,
multi-service gasket sheet, designed to handle the extremes of
pressure and temperature, and it cuts very easily and cleanly. The
versatility of this sheet enables a plant to standardize on one
sheet for a multitude of applications and avoid the confusion of
having to choose from several different sheets. NA1100 is suitable
for service handling the following general media categories:
| |
Mild inorganic acids
|
Mild organic acids
|
Air
|
| |
Diluted alkalis
|
Water
|
Brine
|
| |
Saturated steam
|
Industrial gases
|
Animal oils
|
| |
Synthetic oils
|
Vegetable oils
|
Petroleum and Derivatives
|
| |
General chemicals
|
Neutral solutions
|
Refrigerants
|
| |
Aliphatic solvents
|
|
|
| |
|
|
|
|
|
SERVICE
LIMITS |
| Type |
Description |
Value |
| Temperature Limits |
Maximum |
840°F (450°C) |
| |
Continuous Max |
518°F (270°C) |
| Pressure Limits
(Vacuum) |
Maximum |
1900 psi (130 bar) |
| |
Continuous Max |
1000 psi (70 bar) |
| ASTM Line Call Out
F104 |
F712120E23M6 |
|
| Color |
Black |
|
| Available Sheet
Sizes |
Thicknesses |
1/64", 1/32", 1/16",
3/32", 1/8" |
| |
Sheet Sizes |
59" x 63" |
| |
|
59" x 126" |
| |
|
118" x 126" |
|
TYPICAL
PHYSICAL PROPERTIES |
| ASTM Test Method |
Property |
Value |
| - |
Density |
106 lb/ft3
(1.7 gg/cc) |
| F36 |
Compressibility |
5-15% |
| F36 |
Recovery |
min 50% |
| F152 |
Tensile Strength
Across Grain |
2175 psi (15 N/mm2) |
| F495 |
Ignition Loss |
max 50% |
| F146 |
Thickness Increase
After 5 Hour Immersion |
|
| |
ASTM IRM 903 @300°F (150°C)
|
max 15% |
| |
ASTM Fuel B @77°F (25°C)
|
max 15% |
| F146 |
Weight Increase After
5 Hour Immersion |
|
| |
ASTM IRM 903 @300°F (150°C)
|
max 15% |
| |
ASTM Fuel B @77°F (25°C)
|
max 15% |
| F38 |
Creep relaxation |
22% |
| |
Torque Retention (DIN
52913) |
35 N/mm2 |
| F37 |
Sealability at 1000
psi |
0.2 ml/h |
| |
Pressure x Temperature
|
|
The P x T graph shown above indicates the
service limits for this sheet considering pressure and
temperature simultaneously...(Tests were performed with
nitrogen on 1.6mm thick sheet). The "normal" curve
represents the common usage area for this sheet while the
"maximum" curve indicates the maximum limits. For
applications near or above the "maximum" curve, contact Able
Industrial. |
Properties and application parameters shown
throughout this datasheet are typical. Your specific application
should not be undertaken without independent study and evaluation
for suitability. For specific application recommendations consult
Able Industrial. Failure to select proper sealing products could
result in property damage and/or serious personal injury.
Specifications are subject to change without notice. This edition
supersedes all previous issue
|