CONSTRUCTION
Style NA1076
is a compressed non-asbestos
sheet gasket material produced from a combination of aramid and
other synthetic fibers and bonded with neoprene rubber (CR). It is
manufactured through the hot calender process under rigorous quality
control standards that are registered under ISO-9001 certification.
APPLICATION / SERVICE
Style NA1076
sheet is a good all purpose
sheet that is specifically formulated to handle a broad range of
refrigerants. In addition, Style 1076 is suitable for services
handling water, saturated steam, oils, fuels, mild acids and
alkalies.
|
SERVICE
LIMITS |
| Type |
Description |
Value |
| Temperature Limits
|
Minimum/Maximum |
-40°F (-40°C)/700 F
(370 C) |
| |
Continuous Max. |
392°F (200 C) |
| Pressure Limits |
|
Vacuum to 725 psi (50
bar) |
| ASTM Line Call Out |
ASTM
F104-F712120-B4E99M9 |
|
| Color |
Black |
|
| Available Sheet
Sizes |
Thickness |
1/64", 1/32", 1/16",
3/32", 1/8" |
| |
Sheet Sizes
|
59" x 63" |
| |
|
59" x 126" |
|
TYPICAL
PHYSICAL PROPERTIES* |
| ASTM Test Method |
Property |
Value |
| F 36 |
Compressibility |
7-17% |
| F 36 |
Recovery |
46% |
| F 38 |
Creep relaxation |
20% |
| F146 |
Weight Increase After
5 Hour Immersion |
|
| |
|
|
| |
ASTM Fuel B @77°F (25°C)
|
<_20% |
| |
Thickness Increase
After 5 Hour Immersion |
|
| |
ASTM IRM 903 @ 300°F (150°C)
|
<_30% |
| |
|
|
| |
ASTM Fuel B @77°F (25°C)
|
<_20% |
| |
Tensile Strength
Across Grain |
1740 psi |
| |
Density |
106 lb/ft^3 (1.70
gm/cc) |
*This data is a general guide for selection of
materials and does not constitute specification limits. It should
not be used as the sole means of specifying a material for an
application.
Properties and application parameters shown
throughout this datasheet are typical. Your specific application
should not be undertaken without independent study and evaluation
for suitability. For specific application recommendations consult
Able Industrial. Failure to select proper sealing products could
result in property damage and/or serious personal injury.
Specifications are subject to change without notice. This edition
supersedes all previous issue
|